Product Introduction:This dual-layer epoxy powder coating is formulated using multiple types of
Email:services@moutainchem.com
This dual-layer epoxy powder coating is formulated using multiple types of epoxy resins and functional curing agents. The base layer, like other epoxy anti-corrosion coatings, offers excellent corrosion resistance. The outer layer not only maintains corrosion protection but also enhances the protective properties, making it suitable for highly demanding anti-corrosion environments, especially for pipelines crossing mountainous areas, rivers, and hilly regions.
Excellent adhesion between the base layer and the substrate, as well as between the epoxy layers.
Strong resistance to permeation and corrosion.
The outer layer has high hardness and density, is scratch-resistant, and provides good resistance to plant root penetration.
The coating has excellent resistance to high-temperature cathodic disbondment.
| Item | Quality Indicator | Test Method |
|---|---|---|
| Appearance | Uniform color, no lumps | Visual inspection |
| Volatile Content (%) | ≤ 0.6 | Q/CNPC 38-2002 Appendix B |
| Curing Time (230°C) (min) | ≤ 3 | SY/T 0315-2005 |
| Magnetic Substance Content (%) | ≤ 0.002 | GB/T 6570 |
| No. | Test Item | Technical Indicator | Test Method |
|---|---|---|---|
| 1 | Appearance | Smooth, uniform color, no bubbles, cracks; slight orange peel allowed | Visual inspection |
| 2 | Adhesion (Grade) (24h or 48h) | 1-2 | SY/T 0315-2005 |
| 3 | Cathodic Disbondment Resistance (24h or 48h) (mm) | ≤ 6 | SY/T 0315-2005 |
| Cathodic Disbondment Resistance (28d) (mm) | ≤ 8 | SY/T 0315-2005 | |
| Cross-Section Porosity of Base Layer | 1-4 | SY/T 0315-2005 | |
| Bonding Surface Porosity of Base Layer | 1-4 | SY/T 0315-2005 | |
| 4 | Flexibility (2°) (0° or -30°) (Ordinary Grade) | No cracks | Q/CNPC 38-2002 Appendix D |
| Flexibility (1.5°) (0° or -30°) (Enhanced Grade) | No cracks | Q/CNPC 38-2002 Appendix D | |
| Impact Resistance (10J) (Ordinary Grade) | No pinholes | Q/CNPC 38-2002 Appendix E | |
| Impact Resistance (15J) (Enhanced Grade) | No pinholes | Q/CNPC 38-2002 Appendix E | |
| Scratch Resistance (30Kg) (Ordinary Grade) | Scratch depth ≤ 350 µm, no leakage | Q/CNPC 38-2002 Appendix F | |
| 8 | Scratch Resistance (50Kg) (Enhanced Grade) | Scratch depth ≤ 500 µm, no leakage | Q/CNPC 38-2002 Appendix F |
Q/CNPC 38-2002
Complex anti-corrosion environments, especially pipelines crossing mountainous areas, rivers, and hilly regions.
Electrostatic spraying.
The steel pipe surface should be free of oil and moisture; the surface treatment quality should reach Sa2 1/2 level (GB/T 8923); the anchor pattern depth should be 50-90 mm; dust and abrasives on the steel pipe surface should be blown clean.
The product should be stored in a well-ventilated, dry indoor environment with a temperature below 30°C, away from heat sources, corrosive chemicals, and chemical solvents, and protected from strong light exposure; the stacking height should not exceed four layers; avoid long-term pressure, ensure the packaging box is sealed to prevent caking and moisture, which can affect fluidization performance.
If you're ready to take the next step or Request Free Samples, Leave your message below and we’ll reply soon. 20+ years of chemical manufacturing & export experience, a partner you can trust.
Disclaimer: The above content is for reference and communication only among industry insiders, and does not guarantee its accuracy or completeness. According to relevant laws and regulations and the regulations of this website, units or individuals who purchase related items should obtain valid qualifications and qualification conditions.
Company Phone
+86-21-6420 0566
Working hours
Monday to Friday
Mobile phone:
13816217984
Email:
info@qinsun-lab.com